Free Silicon Content: |
≤10% |
Sic Content: |
≥98% |
Thermal Shock Resistance: |
Good |
Color: |
Black |
Bending Strength: |
400 MPa |
Drawing Format: |
2D/(PDF/CAD)3D(IGES/STEP) |
Micron: |
150 |
Application: |
sintering parts |
Flexural Strength: |
350-600 MPa |
Compressive Strength: |
2000 MPa |
Dielectric Constant: |
9.66 |
Mechanical Strength: |
High |
Maximum Operating Temperature: |
1650°C |
Material: |
Silicon Carbide |
Hardness: |
9.5 Mohs |
Free Silicon Content: |
≤10% |
Sic Content: |
≥98% |
Thermal Shock Resistance: |
Good |
Color: |
Black |
Bending Strength: |
400 MPa |
Drawing Format: |
2D/(PDF/CAD)3D(IGES/STEP) |
Micron: |
150 |
Application: |
sintering parts |
Flexural Strength: |
350-600 MPa |
Compressive Strength: |
2000 MPa |
Dielectric Constant: |
9.66 |
Mechanical Strength: |
High |
Maximum Operating Temperature: |
1650°C |
Material: |
Silicon Carbide |
Hardness: |
9.5 Mohs |