High Temperature Stability: |
Excellent |
Size: |
customized |
Low Thermal Expansion: |
Excellent |
Purity: |
96%,99% |
Dielectric Constant: |
9.8 |
Dielectric Strength: |
15 kV/mm |
Elastic Modulus: |
380 GPa |
Method: |
lsostatic presure |
Max Operating Temperature: |
1700°C |
Color: |
White |
Maximum Use Temperature: |
1700c |
Electrical Resistivity: |
10^14 Ohm-cm |
Melting Point: |
2040°C |
Compressive Strength: |
3000 MPa |
Water Absorption: |
0 |
High Temperature Stability: |
Excellent |
Size: |
customized |
Low Thermal Expansion: |
Excellent |
Purity: |
96%,99% |
Dielectric Constant: |
9.8 |
Dielectric Strength: |
15 kV/mm |
Elastic Modulus: |
380 GPa |
Method: |
lsostatic presure |
Max Operating Temperature: |
1700°C |
Color: |
White |
Maximum Use Temperature: |
1700c |
Electrical Resistivity: |
10^14 Ohm-cm |
Melting Point: |
2040°C |
Compressive Strength: |
3000 MPa |
Water Absorption: |
0 |
السيراميك الألومينا هي المواد الأكثر استخداماً في مجموعة السيراميك الراقية، والتي بعد أن تخضع لعملية تجميد، تتميز بنفس الهيكل البلورية ((AlzO3) مثل الزفير والياقوت.تستخدم هذه المواد في مجموعة واسعة من المجالات الصناعية بسبب خصائصها المادية الممتازة مثل العزل الكهربائي العاليقوة ميكانيكية عالية ومقاومة عالية للاستعمال والكيماويات